Nycal™ 1850R60
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Technical Polymers, LLC |
| Trademark: | Nycal™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D5UBZW_Nycal-1850R60.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nycal™ 1850R60 is a Polyamide 6 (Nylon 6) material filled with 60% glass fiber. It is available in North America for injection molding. Primary attribute of Nycal™ 1850R60: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.70 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 220 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 1.0 to 3.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 12500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 14 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 218 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 215 | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 65.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NuSil MED50-5438 | NuSil Technology | Silicone Rubber, LSR | NuSil |
| ICORENE® 4007 | ICO Polymers EMEA, A Division of A. Schulman | PP Impact Copolymer | ICORENE® |
| Lucofin® 1414 | Lucobit AG | Polyolefin, Unspecified | Lucofin® |
| Lupoy® 1621-02 | LG Chem Ltd. | PC | Lupoy® |
| CERTENE™ PHM-12 | Muehlstein | PP Homopolymer | CERTENE™ |