CABELEC® XS6033
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Cabot Corporation |
| Trademark: | CABELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D4hAMc_CABELEC-XS6033.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CABELEC® XS6033 is an electrically conductive compound based on carbon black dispersed in a modified polypropylene resin. It is characterized by a V0 flammability rating at 3mm under UL94 conditions. The electrical properties are permanent and are not dependent on atmospheric conditions. CABELEC® XS6033 is recommended for packaging and product handling applications where freedom from the hazard of electrostatic discharge is necessary and where flame retardant properties are requested. Examples of use are in handling explosives, chemical powders and electronic components and systems. XS6033 has been designed for injection molding applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.23 | g/cm³ | Internal Method |
| Melt Mass-Flow Rate (MFR) 2 | ISO 1133 | ||
| 230°C/10.0 kg | 20 | g/10 min | |
| 230°C/2.16 kg | 0.30 | g/10 min | |
| 230°C/5.0 kg | 3.0 | g/10 min | |
| Molding Shrinkage - Flow 3 | 1.1 to 1.4 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 4(Shore D, 15 sec) | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 5 | ISO 527-2 | ||
| Yield | 19.4 | MPa | |
| Break | 16.7 | MPa | |
| Tensile Strain 6(Break) | 210 | % | ISO 527-2 |
| Flexural Modulus 7 | 1150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 8(23°C) | 30 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 9(1.8 MPa, Unannealed) | 45.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature 10 | 151 | °C | ISO 306/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 11(0.400 mm) | 2.0E+2 | ohms | IEC 60093 |
| Volume Resistivity 12 | 12 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 180 | °C | |
| Middle Temperature | 180 | °C | |
| Front Temperature | 180 | °C | |
| Nozzle Temperature | 200 | °C | |
| Mold Temperature | 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | CTM E023 |
| 2 . | CTM E005 |
| 3 . | CTM E047 |
| 4 . | CTM E030 |
| 5 . | CTM E041 |
| 6 . | CTM E041 |
| 7 . | CTM E040A |
| 8 . | CTM E044A |
| 9 . | CTM E038 |
| 10 . | CTM E039 |
| 11 . | Extruded Tape, CTM E042E |
| 12 . | Injection molded, CTM E043B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPH 4069 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Epoxies, Ect. 20-3035 (Cat.140) | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| KPOL-NYLON K-NY66/21VC | KPOL Chem Co. | Nylon 66 | KPOL-NYLON |
| LubriOne™ GF-1010 40 MS 2 HS Black 37 | PolyOne Corporation | Nylon 6 | LubriOne™ |
| PermaStat PLUS® 2501 A | RTP Company | PC+ABS | PermaStat PLUS® |