reSound™ X RS1200-0215
| Category: | PLA Comp , Polylactic Acid Compound |
| Manufacturer: | PolyOne Corporation |
| Trademark: | reSound™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D2aAwQ_reSound-X-RS1200-0215.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Edgetek™ Copolyester Compounds are based on Eastman Tritan™ copolyester resin customized to meet specific performance criteria. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 59.3 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 7.0 | % | ASTM D638 |
| Flexural Modulus 3 | 3040 | MPa | ASTM D790 |
| Flexural Strength 4 | 97.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 48 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.18 mm) | 118 | °C | ASTM D648 |
| Additional Information |
|---|
| This product contains 30% by weight renewable resource content. |
| Note Message | |
|---|---|
| 1 . | 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadraflex™ ALE-75A-B20 | Biomerics, LLC | TPU-Polyether | Quadraflex™ |
| Staramide A28K | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| DJSilicone NE-181 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| ExxonMobil™ LLDPE LL 3001.63 | ExxonMobil Chemical | LLDPE | ExxonMobil™ LLDPE |
| Diaterm® A27 GF30TF10 | DTR S.r.l. (Develop Thermoplastic Resins) | Nylon 6 | Diaterm® |