SCHULAMID® 66 GF 50 H TS
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D1h2fb_SCHULAMID-66-GF-50-H-TS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 50% glass fiber reinforced, heat stabilized, surface improved Polyamide 66 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.57 | -- | g/cm³ | ISO 1183/A |
| Viscosity Number | 140 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 17000 | -- | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 230 | -- | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.2 | -- | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 14600 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 330 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 12 | -- | kJ/m² | |
| 23°C | 14 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 75 | -- | kJ/m² | |
| 23°C | 85 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | > 250 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | > 250 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | > 250 | -- | °C | ISO 306/A50, ISO 306/B50 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CONAP® EN-5310 | Cytec Industries Inc. | PUR, Unspecified | CONAP® |
| DOWLEX™ 2006G | The Dow Chemical Company | HDPE | DOWLEX™ |
| Karina BLACK PVC COMPOUND 810D48/ 1-C-AC-AS-HSF | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ PF001S compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |
| Kinta NB5010G | Kinta Technology (Hong Kong) Co., Ltd. | PC | Kinta |