Adflex Q 300 F
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Adflex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D1C8oa_Adflex-Q-300-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Adflex Q 300 F is a thermoplastic polyolefin which has been developed for the extrusion or calendering of soft film. Adflex Q 300 F can also be used as impact/toughener modifier of polypropylene homopolymer in extrusion applications. In strapping applications for instance, it notably decreases fibrillation and improves the processability of the film at high drawing ratios. Adflex Q 300 F can be processed on any conventional PP extrusion line as well as on PVC calendars. It can also be blown on standard LDPE or LLDPE film lines. For regulatory compliance information see the Adflex Q 300F Regulatory Affairs Product Stewardship Information/Certification Data Sheet (RAPIDS), which can be found on www.polymers.lyondellbasell.com. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.890 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.80 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 36 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/25 | ||
| 0.0500 mm 1 | 200 | MPa | |
| 0.0500 mm 2 | 320 | MPa | |
| Tensile Stress | |||
| Yield | 9.00 | MPa | ISO 527-2 |
| Break, 0.0500 mm 3 | 18.0 | MPa | ISO 527-2/500 |
| Break, 50.0 mm 4 | 27.0 | MPa | ISO 527-2/500 |
| Tensile Strain | |||
| Across Flow : Yield, 0.0500 mm | 28 | % | ISO 527-2/500 |
| Flow : Yield, 0.0500 mm | 20 | % | ISO 527-2/500 |
| Break | 500 | % | ISO 527-2 |
| Flexural Modulus | 330 | MPa | ISO 178 |
| Elongation at Break 5 | ISO 527-3 | ||
| MD | 870 | % | |
| TD | 850 | % | |
| Tensile Strength at Yield 6 | ISO 527-3 | ||
| MD | 11.0 | MPa | |
| TD | 8.00 | MPa |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -50°C | 40 | kJ/m² | |
| -20°C | 70 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 50.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 75.0 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm) | 4 | ASTM D2457 | |
| Haze (50.0 µm) | 95 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | TD |
| 2 . | MD |
| 3 . | TD |
| 4 . | MD |
| 5 . | 500mm/min |
| 6 . | 500mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenite™ Propionate 382E2R30015 Natural, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| Sylvin 8333-80FU White 1513 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Arnite® AV2 370 XL | DSM Engineering Plastics | PET | Arnite® |
| Fibremod™ GB364WG | Borealis AG | PP, Unspecified | Fibremod™ |
| Monprene® OM-10185 | Teknor Apex Company | TPE | Monprene® |