Chemlon® 66A 9516 Datasheet,Nylon 66,Teknor Apex Company (Chem Polymer)-SHANGHAI SUSHENG

Message
66A 9516 is an injection moulding grade of nylon 66 containing molybdenum disulphide to reduce the coefficient of friction and improve wear resistance. It is well suited to applications involving moving parts such as bearings, bushes, gear wheels, etc.

General Information
Additive	Molybdenum disulfide lubricant
Features	Low friction coefficient Good wear resistance Lubrication
Uses	Bushing Gear Bearing
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.15	g/cm³	ISO 1183
Molding Shrinkage ¹	1.4 - 1.9	%	Internal method
Water Absorption (Equilibrium, 23°C, 50% RH)	2.5	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3000	MPa	ISO 527-2
Tensile Stress	75.0	MPa	ISO 527-2
Flexural Modulus	2700	MPa	ISO 178
Flexural Stress	75.0	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength	9.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength	No Break		ISO 179/1eU
Notched Izod Impact	5.0	kJ/m²	ISO 180/A
Unnotched Izod Impact Strength	35	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	190	°C	ISO 75-2/B
1.8 MPa, not annealed	75.0	°C	ISO 75-2/A

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+14	ohms	IEC 60093
Volume Resistivity	1.0E+16	ohms·cm	IEC 60093
Dielectric Strength (3.00 mm)	17	kV/mm	IEC 60243-1
Comparative Tracking Index	600	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.50 mm, Teknor Apex test result)	HB		UL 94
Oxygen Index	24	%	ISO 4589-2

Injection	Nominal Value	Unit
Drying Temperature	80.0	°C
Drying Time	2.0	hr
Rear Temperature	270 - 290	°C
Middle Temperature	270 - 290	°C
Front Temperature	270 - 290	°C
Processing (Melt) Temp	270 - 290	°C
Mold Temperature	80.0 - 90.0	°C
Injection Rate	Fast
Back Pressure	Low
Screw Speed	Moderate

Injection instructions
No drying is necessary unless the material has been exposed to air for longer than three hours. The appearance of splash marks on the surface of mouldings indicates excessive moisture is present.

Note Message
1 .	Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

Note Message

1 .

Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

Category:	Nylon 66 , Polyamide 66
Manufacturer:	Teknor Apex Company (Chem Polymer)
Trademark:	Chemlon®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	D0a3MV_Chemlon-66A-9516.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Maxelast® P3760	Nantong Polymax Elastomer Technology, Co., Ltd	TPE	Maxelast®
POLYVIN® PVC 9031D	A. Schulman Inc.	PVC, Unspecified	POLYVIN®
Xuchuan XCW-8060HT	Xuchuan Chemical (Suzhou) Co., Ltd	PUR, Unspecified	Xuchuan
Diamond ASA C1030	Network Polymers, Inc.	ASA	Diamond ASA
LEXAN™ 103 resin	SABIC Innovative Plastics	PC	LEXAN™