CP PRYME® Polyethylene PE100LD-.7FM
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Chase Plastics Services Inc. |
| Trademark: | CP PRYME® Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D0C9Gd_CP-PRYME-Polyethylene-PE100LD--7FM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CP PRYME® Polyethylene PE100LD-.7FM is a Low Density Polyethylene product. It is available in North America. |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 52 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 2% Secant (23°C) | 132 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 9.45 | MPa | |
| Break, 23°C | 13.2 | MPa | |
| Tensile Elongation (Break, 23°C) | 650 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 |
| Melting Temperature | 107 | °C | DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UmaPET COLM | Ester Industries Ltd. | PET | UmaPET |
| CompaMid® PA 6.6 GF 10 M 20 | DimeLika Plast GmbH | Nylon 66 | CompaMid® |
| Karina IVORY PVC COMPOUND 851-35/1-E-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lupoy® 1320C-07 | LG Chem Ltd. | PC | Lupoy® |
| Osterlene® HIPS2.63.6 | Osterman & Company | PS (HIPS) | Osterlene® |