| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Covestro - PUR |
| Trademark: | Baytec® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CvLqUO_Baytec-EDG-070D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Baytec EDG-070D is a two-component, one-shot system which yields a solid polyurethane elastomer. It is a UV-stable polyurethane system with an approximate hardness of 70 Shore D. The isocyanate component is an aliphatic HDI-based polyisocyanate, and the polyol component is a polyether/polyester polyol blend. The Baytec EDG-070D system is used in table-edging applications. As with any product, use of the Baytec EDG-070D system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore D) | 70 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 28.2 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 160 | % | ASTM D412 |
| Tear Strength | |||
| -- 1 | 84.9 | kN/m | ASTM D624 |
| Cracking | 14 | kN/m | ASTM D1938 |
| Thermoset | Nominal Value | ||
|---|---|---|---|
| Thermoset Components 2 | |||
| Component a | Mixing ratio by weight: 100 | ||
| Component B | Mixing ratio by weight: 100 |
| Additional Information |
|---|
| Part A Type: Isocyanate Appearance: Clear, pale yellow liquid Specific Gravity @ 25°C: 1.17 Viscosity @25°C: 2900 mPa Flash Point, SETA: 238°C NCO: 21.5 wt% Part B Type: Polyol Appearance: Pale yellow liquid Specific Gravity @ 25°C: 1.05 Viscosity @25°C: 3000 mPa-s Flash Point, PMCC: 186°C Water: 0.07 wt% max Hydroxyl Number: 270 mg KOH/g IsocyanateTemperature: 41 to 46°CPolyol Temperature: 38 to 44°CMold Temperature: 44 to 60°CGel Time: 75 to 150 secDemold Time: 6 to 15 min |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | 105 Index |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® Homo 1.8 | Marco Polo International, Inc. | PP Homopolymer | MARPOL® Homo |
| SIVIC® 8010 | SIDIAC | NBR | SIVIC® |
| Nipol® NBR N21 | Zeon Corporation | NBR | Nipol® NBR |
| CP PRYME® Polyethylene PE100HDC-.35FM | Chase Plastics Services Inc. | HDPE | CP PRYME® Polyethylene |
| Fluon® LM-ETFE 730AP | Asahi Glass Co., Ltd. | ETFE | Fluon® |