Mafill® CT 4210
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Ravago Group |
| Trademark: | Mafill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ct8DNp_Mafill-CT-4210.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PP Copo 20% Talc V0 Deca-BDE free |
| General Information | |
|---|---|
| Additive |
|
| Recycled Content |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.80 to 1.2 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 24.0 | MPa | |
| Break | 18.0 | MPa | |
| Tensile Strain (Break) | 10 | % | ISO 527-2 |
| Flexural Modulus | 2500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 58.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 65.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 66 MV 2 | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| T-Blend® 4801B-SP | TSRC Corporation | SBS | T-Blend® |
| TRANSMARE® 22CT20-0.001 | Transmare Compounding B.V. | PP Copolymer | TRANSMARE® |
| ADENE BHQBG | A.D. Compound spa | PP Copolymer | ADENE |
| Plenco 08112 (Compression) | Plastics Engineering Co. | Polyester, TS | Plenco |