Ingeo™ 4032D
| Category: | PLA , Polylactic Acid |
| Manufacturer: | NatureWorks® LLC |
| Trademark: | Ingeo™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CsZtIU_Ingeo-4032D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ingeo 4032D can be converted into a biaxially oriented film with use temperatures up to 300°F (150°C). This film has excellent optics, good machinability and excellent twist and deadfold. These properties make 4032D film an ideal product for laminations and other packaging applications. Additional properties include barrier to flavor and grease and oil resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ASTM D1505 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| MD : 25 µm | 3450 | MPa | ASTM D882 |
| TD : 25 µm | 3790 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 103 | MPa | ASTM D882 |
| TD : Yield, 25 µm | 145 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 180 | % | ASTM D882 |
| TD : Break, 25 µm | 100 | % | ASTM D882 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 17 | g | ASTM D1922 |
| TD : 25 µm | 14 | g | ASTM D1922 |
| Carbon Dioxide Transmission Rate | 2850 | cm³/m²/24 hr | Internal method |
| Oxygen Permeability | 675 | cm³/m²/24 hr | ASTM D1434 |
| Water Vapor Transmission Rate | 380 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Spencer Impact | 2.50 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 155 - 170 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 25.4 µm) | 90 | ASTM D2457 | |
| Haze (25.4 µm) | 2.1 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.025 | % | |
| Cylinder Zone 1 Temp. | 179 | °C | |
| Cylinder Zone 2 Temp. | 191 | °C | |
| Cylinder Zone 3 Temp. | 199 | °C | |
| Adapter Temperature | 199 | °C | |
| Melt Temperature | 202 - 218 | °C | |
| Die Temperature | 199 | °C |
| Extrusion instructions |
|---|
| Screw Speed 20-100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPH 5042 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Vamac® GXF | DuPont Performance Elastomers | AEM | Vamac® |
| HONES® Conductive Nylon | Guangdong Shunde Hones Polymer Material Co., Ltd. | Nylon, Unspecified | HONES® |
| INSULCAST® RTVS Primer 40 | ITW Polymers Coatings North America | Silicone | INSULCAST® RTVS |
| Axiall PVC 67800 | Axiall Corporation | PVC, Flexible | Axiall PVC |