SABIC® LDPE 2201H1W
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CsArdy_SABIC-LDPE-2201H1W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LDPE 2201H1W is a grade with a low level of anti block and a medium level of slip agent (E=erucamide). The grade has a very good draw down ability. Films based on 2201H1W combine toughness with high tear strength, good optical properties and low CoF. Application SABIC® LDPE 2201H1W is typically used for lamination films, high quality carrier bags and high quality packaging films. SABIC® LDPE 2201H1W can typically be used for food applications due to very low migration levels. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.85 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 0.15 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 50 µm, blown film | 170 | MPa | ISO 527-3 |
| TD : 50 µm, blown film | 170 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm, blown film | 11.0 | MPa | ISO 527-3 |
| TD : Yield, 50 µm, blown film | 11.0 | MPa | ISO 527-3 |
| MD : Broken, 50 µm, blown film | 25.0 | MPa | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 20.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | > 200 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | > 500 | % | ISO 527-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength - Blown FIlm (50.0 µm) | 250 | J/cm | ASTM D4272 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blocking - Blown Film (50.0 µm) | 50 | g | Internal method |
| Re-blocking - Blown Film (50.0 µm) | g | Internal method | |
| Tear Strength 1 | ISO 6383-2 | ||
| MD : 50.0 µm | 45.0 | kN/m | ISO 6383-2 |
| TD : 50.0 µm | 45.0 | kN/m | ISO 6383-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Blown Film) | 65 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 6.0 | % | ASTM D1003A |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film properties have been measured at film of 50 µm with a BUR of 3.The film has been produced on Kiefel IBC blown film line with 200 kg/h. Die size 200 mm, die gap 0.8 mm. |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 885 DEL | RTP Company | Acetal (POM) Homopolymer | RTP |
| Adell PP ER-18 | Adell Plastics, Inc. | PP Homopolymer | Adell PP |
| Beamset 1200 | Arakawa Chemical Industries, Ltd. | Epoxy | Beamset |
| Electroblend® ABS-2800 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | ABS | Electroblend® |
| Sinpolene GPP2010/3 | Teknor Apex Asia Pacific PTE. LTD. | TPO | SINPOLENE |