| RX® 655 is a fiberglass and mineral reinforced phenolic molding compound, with excellent dimensional stability and good strength at elevated temperatures. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.10 | g/cm³ | ISO 1183 |
| Apparent Density | 0.95 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.060 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 105 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, Compression Molded) | 90.0 | MPa | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 27000 | MPa | ISO 178 |
| Flexural Stress (Compression Molded) | 165 | MPa | ISO 178 |
| Compressive Stress | 410 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (Compression Molded) | 2.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | ISO 75-2/A | ||
| 1.8 MPa, Unannealed | 200 | °C | |
| 1.8 MPa, Annealed | > 282 | °C | |
| CLTE - Flow | 1.7E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.94 | W/m/K | ASTM C518 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 14 | kV/mm | ASTM D149 |
| Arc Resistance | 180 | sec | ASTM D495 |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® LDC 770 | Marco Polo International, Inc. | LDPE | MARPOL® |
| Precision Polymer V97B | Precision Polymer Engineering Ltd. | Fluorelastomer | Precision Polymer |
| VITAMIDE® AI10BK6201/2C | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Trilene FreeFlow™ 66 | Lion Copolymer, LLC | EPM | Trilene FreeFlow™ |
| LEXAN™ HP2 resin | SABIC Innovative Plastics | PC | LEXAN™ |