SUPREME Specialty PS SP243
| Category: | PS (Specialty) , Specialty Polystyrene |
| Manufacturer: | Supreme Petrochem Ltd. |
| Trademark: | SUPREME Specialty PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CqKSvT_SUPREME-Specialty-PS-SP243.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SUPREME Specialty PS SP243 is a special polystyrene product,. It can be processed by extrusion or injection molding and is available in North America, Africa and the Middle East, Europe or Asia Pacific. The application fields of SUPREME Specialty PS SP243 include movies, hats/caps/corks, containers and food contact applications. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 4.5 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(23°C, 3.20 mm, Injection Molded) | 425 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, 3.20 mm, Injection Molded) | 5.0 | % | ASTM D638 |
| Flexural Modulus (23°C, 3.20 mm, Injection Molded) | 22000 | MPa | ASTM D790 |
| Flexural Strength (23°C, 3.20 mm, Injection Molded) | 600 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 15 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.20 mm) | 200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm, Injection Molded) | 81.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 103 | °C | ASTM D1525 3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (1000 µm) | 88.0 | % | ASTM D1003 |
| Haze (1000 µm, Injection Molded) | 2.5 | % | ASTM D1003 |
| Additional Information |
|---|
| The values listed as Haze and Transmittance ASTM D1003, were tested in accordance with SPL testing methods. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | < 220 | °C | |
| Mold Temperature | 40.0 - 50.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | < 220 | °C |
| Extrusion instructions |
|---|
| Mold Temp: 40 to 50°C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 标准 B (120°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PROTEQ™ L10Q6 | Marplex Australia Pty. Ltd. | PP Copolymer | PROTEQ™ |
| Shin-Etsu RTV KE-348 | Shin-Etsu Silicones of America | Silicone Rubber, RTV-1 | Shin-Etsu RTV |
| Nipol® 1002 | Zeon Chemicals L.P. | NBR | Nipol® |
| Jam PE 23507 | Jam Petrochemical Company | LLDPE | Jam PE |
| Luranyl® HT 220 G6 | ROMIRA GmbH | PPE+Nylon 66 | Luranyl® |