ACCUTECH™ CP0405UVV
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUTECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CoBEXU_ACCUTECH-CP0405UVV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ACCUTECH™CP0405UVV is a polypropylene copolymer (PP Copoly) product,. It is available in North America. Typical application areas are: automotive industry. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.6 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1500 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 26.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 130 | % | ASTM D638 |
| Flexural Modulus | 1500 | MPa | ASTM D790 |
| Flexural Strength | 38.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 190 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 100 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 58.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Flammability, ASTM FMVSS: PASS |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene GC43P250-01 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| SHIN-A SEV-6500M80 | SHIN-A T&C | Epoxy | SHIN-A |
| TABOREN PC 42 B 35 | SILON s.ro | PP Copolymer | TABOREN |
| Tarnamid® T- 27 MT 30 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| Domamid HT™ 7750R50H3 | Technical Polymers, LLC | Nylon 66 | Domamid HT™ |