Rilsan® CLEAR C 170 MED
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CmT4yG_Rilsan-CLEAR-C-170-MED.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan ® Clear G 170 MED is a high performance transparent polyamide with outstanding thermal resistance. This grade offers the highest quality and is specifically designed to meet the stringent requirements of the medical applications. Upon request letters regarding USP Class VI compliance can be provided. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 40°C, 24 hr, 4.00 mm | 0.72 | % | |
| Flow : 40°C, 24 hr, 4.00 mm | 0.69 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 3.8 | % | |
| Equilibrium, 23°C, 50% RH | 1.7 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 84 | ||
| Shore D, 15 sec | 79 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2020 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 74.0 | MPa | |
| Break | 58.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 9.0 | % | |
| Break | > 100 | % | |
| Flexural Modulus | 1980 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 13 | kJ/m² | |
| 23°C | 13 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 150 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 136 | °C | ISO 75-2/A |
| Glass Transition Temperature | 168 | °C | ISO 11357-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2000 µm, 560 nm) | 90.8 | % | ASTM D1003 |
| Refractive Index | 1.5380 | ISO 489 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 270 to 310 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Melt Temperature | 270 to 290 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8815-80 Grey 9491 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Moplen HP565K | LyondellBasell Industries | PP Homopolymer | Moplen |
| apigo® CA 450 | API SpA | TPO (POE) | apigo® |
| DOW™ Electrical & Telecommunications DGDA-1310 BK | The Dow Chemical Company | HDPE | DOW™ Electrical & Telecommunications |
| LNP™ LUBRICOMP™ RAL23S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |