Bapolene® PP5026
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Bamberger Polymers, Inc. |
| Trademark: | Bapolene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CkldHK_Bapolene-PP5026.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene extrusion impact copolymer with excellent color and processability. This resin also has a superior balance of stiffness and impact strength. This product meets FDA regulation 21 CFR 177.1520 and is suitable for food contact applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.902 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 102 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 26.9 | MPa | ASTM D638 |
| Flexural Modulus - 1% Secant | 1320 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 75.0 | °C | |
| 1.8 MPa, Unannealed | 46.0 | °C |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXTEL® 600T15IMUV | MRC Polymers, Inc. | TPO | MAXTEL® |
| TES J-1200/10/V0/ND BK2089 | Techmer Engineered Solutions | ABS | TES |
| Chemlon® 182 | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| DEXFLEX® D60-UV | LyondellBasell Industries | TPO (POE) | DEXFLEX® |
| Plexar® PX6002 | LyondellBasell Industries | PP, Unspecified | Plexar® |