GLAMIDE® T-803
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | GLAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ckk0GM_GLAMIDE-T-803.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GLAMIDE®T-803 is a polyamide 6 (nylon 6) product,. It is available in North America. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.14 | -- | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 44 | -- | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | |||
| 1.00 mm | 0.40 - 0.70 | -- | % | ASTM D955 |
| 3.00 mm | 1.2 - 1.4 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 24 hr | 1.8 | -- | % | ASTM D570 |
| Equilibrium, 65% RH | 3.5 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ASTM D638 | |||
| Yield, -40°C | 120 | 110 | MPa | ASTM D638 |
| Yield, 23°C | 90.0 | 45.0 | MPa | ASTM D638 |
| Yield, 80°C | 35.0 | 25.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 30 | 200 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | |||
| -40°C | 4000 | 3600 | MPa | ASTM D790 |
| 23°C | 3200 | 1100 | MPa | ASTM D790 |
| 80°C | 900 | 500 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | |||
| Yield, -40°C | 140 | 125 | MPa | ASTM D790 |
| Yield, 23°C | 113 | 49.0 | MPa | ASTM D790 |
| Yield, 80°C | 55.0 | 30.0 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 85.0 | -- | MPa | ASTM D695 |
| Taber Abrasion Resistance (1000 Cycles, CS-17 Wheel) | 5.00 | -- | mg | ASTM D1044 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 30 | 45 | J/m | ASTM D256 |
| 23°C | 50 | 390 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 180 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 75.0 | -- | °C | ASTM D648 |
| CLTE - Flow | 8.3E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 18 | 12 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 3.80 | 8.00 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 0.020 | -- | ASTM D150 | |
| Arc Resistance | 125 | 105 | sec | ASTM D495 |
| Comparative Tracking Index | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 Comparative Tracking Index, IEC Method: >600 V |
| 调节后的 Tensile Elongation, ASTM D638, 23°C: >200 %Volume Resistivity, ASTM D257: 1e9 to1e10 ohm-mComparative Tracking Index, IEC Method: >600 V |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 80.0 | °C | |
| Injection Pressure | 30.0 - 40.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® PET IV 78 HF | Marco Polo International, Inc. | PET | MARPOL® PET |
| PRE-ELEC® PS 1326 | Premix Oy | PS Alloy | PRE-ELEC® |
| RTP EMI 2560.75 | RTP Company | PC+ABS | RTP |
| Lucent PC PC-FR2 | Lucent Polymers, Inc. | PC | Lucent PC |
| Sylvin 9604-90 Yellow 405 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |