Chemlon® 206 G
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Chemlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CkNdOg_Chemlon-206-G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Chemlon® 206 G is a Polyamide 6 (Nylon 6) material filled with 6.0% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Chemlon® 206 G: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.80 to 1.3 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 93.1 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 4.0 | % | |
| Break | 5.0 | % | |
| Flexural Modulus | 3310 | MPa | ASTM D790 |
| Flexural Strength | 128 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 179 | °C | ASTM D648 |
| Melting Temperature | 216 | °C | DSC |
| CLTE - Flow | 5.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+18 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.00 mm) | 11 | kV/mm | ASTM D149 |
| Comparative Tracking Index (CTI) | 600 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.810 mm) | HB | UL 94 | |
| Oxygen Index | 24 | % | ASTM D2863 |
| FMVSS Flammability | PASSES | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 218 to 235 | °C | |
| Middle Temperature | 252 to 257 | °C | |
| Front Temperature | 252 to 266 | °C | |
| Nozzle Temperature | 252 to 266 | °C | |
| Processing (Melt) Temp | 249 to 266 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ TA210HS | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| WanBlend® WHT-890E5 | Wanhua Chemical Group Co., Ltd. | TPU-Polyether | WanBlend® |
| Durolon® I2700 | Unigel Plásticos | PC | Durolon® |
| Elastane™ 4720-94A | Technical Polymers, LLC | TPU-Polyester | Elastane™ |
| Stat-Tech™ PP-16CP/000-2HI BLK | PolyOne Corporation | PP, Unspecified | Stat-Tech™ |