HIPOLEN P® FB 4T
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | HIPOL A.D. |
| Trademark: | HIPOLEN P® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CkI8X1_HIPOLEN-P-FB-4T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hipolen® P FB 4T is a controlled crystalline homopolymer, intended for thermoforming packaging. Typical applications of Hipolen® P FB 4T are highly transparent cups and containers. Hipolen® P FB 4T has a wide range of approval for contact with food but for specific applications, reference should be made to Hipol chemical industry. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.5 - 2.5 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 25.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 9.0 | % | ASTM D638 |
| Fracture | 500 | % | ASTM D638 |
| Flexural Modulus | 1750 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 30 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 100 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 155 | °C | ISO 306/A50 |
| Additional Information |
|---|
| The value listed as Mold Shrink, Linear-Flow may not have been tested according to ASTM D955. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 - 250 | °C |
| Extrusion instructions |
|---|
| Extrusion:1st Chill-roll temperature: 40 to 70°C2nd Chill-roll temperature: 50 to 90°C3rd Chill-roll temperature: 40 to 70°CThermoforming:Solid phase forming temperature: 140 to 160°CMelt phase forming temperature: 180 to 230°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-167U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| ISPLEN® PR 264 M1F | REPSOL | PP Random Copolymer | ISPLEN® |
| Iupilon® CGH1020KR | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| Plexiglas® DR-100G | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |
| TECHNYL® C 218 V35 NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |