LNP™ STAT-KON™ ME003S compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ck0RAm_LNP-STAT-KON-ME003S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON ME003S is a compound based on Polypropylene resin containing 15% Carbon Fiber. Added features of this material include: Electrically Conductive, Heat Stabilized. Also known as: LNP* STAT-KON* Compound MC-1003 HS Product reorder name: ME003S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.990 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.40 to 0.60 | % | ASTM D955 |
| Across Flow : 24 hr | 0.50 to 0.70 | % | ASTM D955 |
| Across Flow : 24 hr | 0.60 | % | ISO 294-4 |
| Flow : 24 hr | 0.52 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8960 | MPa | ASTM D638 |
| -- | 8590 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 47.6 | MPa | ASTM D638 |
| Yield | 47.0 | MPa | ISO 527-2 |
| Break | 39.3 | MPa | ASTM D638 |
| Break | 44.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 0.70 | % | ASTM D638 |
| Yield | 0.78 | % | ISO 527-2 |
| Break | 1.3 | % | ASTM D638 |
| Break | 1.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 6890 | MPa | ASTM D790 |
| -- | 7000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 65.5 | MPa | ASTM D790 |
| -- | 62.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 16 | J/m | ASTM D256 |
| 23°C 2 | 1.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D4812 |
| 23°C 3 | 8.6 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 14.8 | J | ASTM D3763 |
| -- | 3.20 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 154 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 150 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 134 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 131 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 2.9E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 238 to 249 | °C | |
| Processing (Melt) Temp | 227 to 249 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BY36GY6619 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| UBE Polyethylene F023 | UBE America, Inc. | PE, Unspecified | UBE Polyethylene |
| GELAST 1350 | Guang Sung Plastics (GSPL) | TPV | GELAST |
| LNP™ THERMOCOMP™ MF006AS compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOCOMP™ |
| Petroquim PP PH 0322 | Petroquim S.A. | PP Homopolymer | Petroquim PP |