Durethan® BKV 130 CS DUS008 600091
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CiYULd_Durethan-BKV-130-CS-DUS008-600091.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 30 % glass fibers, injection molding, improved impact strength |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | ||
| Across Flow : 280°C, 2.00 mm 1 | 0.75 | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.090 | % | |
| Flow : 280°C, 2.00 mm 3 | 0.25 | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.050 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 9200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 145 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.5 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 8500 | MPa | ISO 178/A |
| Flexural Stress 6(23°C) | 245 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 3.3 | % | ISO 178/A |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PA 6-HI, GR, 14-100, GF30 | ISO 1874 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | < 10 | kJ/m² | |
| 23°C | < 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 55 | kJ/m² | |
| 23°C | 75 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | < 10 | kJ/m² | |
| 23°C | 12 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 60 | kJ/m² | |
| 23°C | 65 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 210 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | °C | ISO 75-2/A |
| Melting Temperature 8 | 220 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 2.0E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.1E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 7002A-02 | Colorite Polymers | PVC, Unspecified | Unichem |
| Generic PUR-Ester/MDI | Generic | PUR-Ester/MDI | Generic |
| Latigloss 57 G/60 F2 | LATI S.p.A. | PPA | Latigloss |
| LNP™ THERMOCOMP™ LX97024 compound | SABIC Innovative Plastics Europe | PEEK | LNP™ THERMOCOMP™ |
| LNP™ LUBRICOMP™ DFL28EG compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |