ResinDirect GPPS7
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | ResinDirect |
| Trademark: | ResinDirect |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CiQruW_ResinDirect-GPPS7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ResinDirect GPPS7 is a General Purpose Polystyrene material. It is available in North America. Important attributes of ResinDirect GPPS7 are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 7.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 37.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield) | 2.0 | % | ASTM D638 |
| Flexural Modulus 3 | 3450 | MPa | ASTM D790 |
| Flexural Strength 4 | 75.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 21 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 85.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 102 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 5.1 mm/min |
| 2 . | 5.1 mm/min |
| 3 . | 2.5 mm/min |
| 4 . | 2.5 mm/min |
| 5 . | Rate B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Royalstat R675 | Spartech Plastics | PS (HIPS) | Royalstat |
| Moplen RP5007 | PolyMirae | PP Random Copolymer | Moplen |
| Baydur® 730 IBS (35 pcf) | Covestro - PUR | PUR-MDI | Baydur® |
| Electrafil® J-71/CF/40/EG | Techmer Engineered Solutions | Nylon 6 Alloy | Electrafil® |
| Karina BLACK PVC COMPOUND 909D48/ 1-C-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |