WPP PE PEH1TF2-Natural
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | Washington Penn Plastic Co. Inc. |
| Trademark: | WPP PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ChnB7d_WPP-PE-PEH1TF2-Natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| WPP PE PEH1TF2-Natural is a polyethylene product, which contains 24% talc filler. It can be processed by blow molding or extrusion and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. The main characteristics are: heat stabilizer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.13 | g/cm³ | ASTM D792 |
| -- | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 16 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 32.0 | MPa | ASTM D638 |
| Fracture | 32.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 2 | 14 | % | ASTM D638 |
| Fracture 3 | 40 | % | ASTM D638 |
| Fracture | 14 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 4 | 1950 | MPa | ASTM D790 |
| -- 5 | 1800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 580 | J/m | ASTM D256 |
| -20°C | 26 | kJ/m² | ISO 180 |
| 23°C | 42 | kJ/m² | ISO 180 |
| Multi-Axial Instrumented Impact Energy (0°C) | 14.5 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 98.0 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 85.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 55.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Tested at 23 ± 2°C (73.4 ± 3.6°F) and 50 ± 5% relative humidity unless otherwise noted. |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 2005 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| Milastomer™ W600B | Mitsui Chemicals America, Inc. | TPV | Milastomer™ |
| VESTAKEEP® 4000 FC30 | Evonik Industries AG | PEEK | VESTAKEEP® |
| FERREX® GPP30CN33HB-NA | Ferro Corporation | PP, Unspecified | FERREX® |
| ELIX™ ABS M203FC | ELIX Polymers, S. L. | ABS | ELIX™ ABS |