Rilsan® CLEAR G 300 HI
| Category: | Nylon Copolymer , Polyamide Copolymer |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CglkV7_Rilsan-CLEAR-G-300-HI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan ® Clear G 300 HI is a high performance transparent copolyamide. This grade has been designed for injection molding applications, requiring high impact resistance, while keeping outstanding flexibility, chemical resistance and ultra light weight of Rilsan® Clear range. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 40°C, 24 hr, 4.00 mm | 0.70 | % | |
| Flow : 40°C, 24 hr, 4.00 mm | 0.60 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.90 | % | |
| Equilibrium, 23°C, 50% RH | 0.90 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 77 | ||
| Shore D, 15 sec | 73 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 715 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 24.0 | MPa | |
| Break | 50.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 6.0 | % | |
| Break | > 250 | % | |
| Flexural Modulus | 740 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 19 | kJ/m² | |
| 23°C | 94 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 90.0 | °C | ISO 11357-2 |
| Melting Temperature | 103 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2000 µm, 560 nm) | 91.3 | % | ASTM D1003 |
| Refractive Index | 1.5030 | ISO 489 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 210 to 270 | °C | |
| Mold Temperature | < 30.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUNIGUM® P2100 | Omnova Solutions Inc. | Acrylic, Unspecified | SUNIGUM® |
| Syncure™ S1006B | PolyOne Corporation | XLPE | Syncure™ |
| Adiprene® Duracast® S930 | Chemtura | PUR-Ester/MDI | Adiprene® Duracast® |
| Hifax TYC 1229P | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |
| RONFALIN® ABS 1412 GF 17 | A. Schulman Europe | ABS | RONFALIN® |