LNP™ THERMOCOMP™ JF008E compound
| Category: | PESU , Polyethersulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CgNLm7_LNP-THERMOCOMP-JF008E-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP JF008E is a compound based on Polyethersulfone containing 40% Glass Fiber. Characteristics of this grade are: Easy Molding. Also known as: LNP* THERMOCOMP* Compound JF-1008 EM Product reorder name: JF008E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.69 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 to 0.30 | % | |
| Across Flow : 24 hr | 0.50 to 0.70 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.32 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.49 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 15400 | MPa | ASTM D638 |
| -- | 13800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 152 | MPa | ASTM D638 |
| Yield | 146 | MPa | ISO 527-2/5 |
| Break 3 | 152 | MPa | ASTM D638 |
| Break | 146 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 1.8 | % | ASTM D638 |
| Yield | 1.5 | % | ISO 527-2/5 |
| Break 5 | 1.8 | % | ASTM D638 |
| Break | 1.5 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 12300 | MPa | ASTM D790 |
| -- 7 | 12200 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 207 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 209 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 208 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 77 | J/m | ASTM D256 |
| 23°C 10 | 7.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 570 | J/m | ASTM D4812 |
| 23°C 11 | 35 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 13.3 | J | ASTM D3763 |
| -- | 2.42 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 212 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 231 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 207 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 211 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 5.0E-6 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.0E-6 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 343 to 354 | °C | |
| Middle Temperature | 360 to 371 | °C | |
| Front Temperature | 371 to 382 | °C | |
| Processing (Melt) Temp | 354 to 371 | °C | |
| Mold Temperature | 138 to 149 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ EPDM0466-NC | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |
| tefabloc® TO 628 | Mitsubishi Chemical Performance Polymers, Inc. | SEBS | tefabloc® |
| Electrafil® ABS SS10 FR BK | Techmer Engineered Solutions | ABS | Electrafil® |
| Kumho SBR 1783 | Korea Kumho Petrochemical Co., Ltd. | SBR, Emulsion | Kumho SBR |
| Iupilon® MB2210R | Mitsubishi Engineering-Plastics Corp | PC+ABS | Iupilon® |