POOYATAK CG203

Category:	PE, Unspecified , Polyethylene
Manufacturer:	Pooya Polymer Tehran
Trademark:	POOYATAK
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	CfYQ2g_POOYATAK-CG203.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Cling MB Description POOYATAK CG203 is a PE based master batch containing a tackifying resin is used as a cling agent. It can be used in LLDPE or LDPE based stretch wrap and cling wrap films for pallet wrapping, silage wrapping and food packaging whether by blown or cast processing. The agent migrates to the film surface within 24 to 72 hours and exhibits the cling properties by then. There must neither be any slip or antiblock agent in the film base resin nor as masterbatch in the formulas. Application POOYATAK CG203 is designed for ease of dilution and homogeneous mixing and is therefore suitable for direct addition using automatic dosing units or by pre-blending. Depending on the film thickness (the thicker film needs less addition level), process (the blown process needs double dosage), film cooling temperature (higher cooling temperature needs more level) and the final application it can be used from 2 to 10%. It should be stored in a dry and cool place not to exceed 6 month.

Message

Cling MB

Description
POOYATAK CG203 is a PE based master batch containing a tackifying resin is used as a cling agent. It can be used in LLDPE or LDPE based stretch wrap and cling wrap films for pallet wrapping, silage wrapping and food packaging whether by blown or cast processing. The agent migrates to the film surface within 24 to 72 hours and exhibits the cling properties by then.
There must neither be any slip or antiblock agent in the film base resin nor as masterbatch in the formulas.

Application
POOYATAK CG203 is designed for ease of dilution and homogeneous mixing and is therefore suitable for direct addition using automatic dosing units or by pre-blending. Depending on the film thickness (the thicker film needs less addition level), process (the blown process needs double dosage), film cooling temperature (higher cooling temperature needs more level) and the final application it can be used from 2 to 10%.
It should be stored in a dry and cool place not to exceed 6 month.

General Information
Features	High Cling
Uses	Masterbatch Stretch Wrap
Appearance	White
Forms	Pellets

Physical	Nominal Value	Unit	Test Method
Density	0.910	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (120°C/1.2 kg)	5.0 to 11	g/10 min	ASTM D1238
Moisture Content	< 2000	ppm	ASTM D644

Additional Information	Nominal Value	Unit	Test Method
Pellet Size	40.0 to 50.0	pcs/cm³	Internal Method

Resin Grade	Manufacturer	Category	Trademark
Tenogel® ABS A3 LF NTLA010 AB348	Petropol Industry and Trade of Polymers LTDA	ABS	Tenogel® ABS
BCC Resins BC 8160	BCC Products Inc.	PUR, Unspecified	BCC Resins
Karina GRAY PVC COMPOUND 800-18/238-A-ERYB (***)	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
LNP™ LUBRICOMP™ UX06427 compound	SABIC Innovative Plastics	PPA	LNP™ LUBRICOMP™
Grilamid® 2S XE 10901 nat	EMS-GRIVORY	Nylon 612	Grilamid®