| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Asia International Enterprise (Hong Kong) Limited |
| Trademark: | AIE PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CfMrFO_AIE-PBT-30G6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AIE PBT 30G6 is a polybutene terephthalate (PBT) material, which contains a filler of 30% glass fabric reinforcement. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is injection molding. The main features of AIE PBT 30G6 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.56 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.30 - 0.60 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 120 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2 |
| Flexural Modulus | 8700 | MPa | ISO 178 |
| Flexural Stress | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 18 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 210 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 140 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 235 - 250 | °C | |
| Middle Temperature | 240 - 260 | °C | |
| Front Temperature | 240 - 260 | °C | |
| Nozzle Temperature | 230 - 245 | °C | |
| Mold Temperature | 50.0 - 160 | °C | |
| Injection Pressure | 40.0 - 120 | MPa | |
| Holding Pressure | 40.0 - 50.0 | MPa | |
| Back Pressure | 5.00 - 10.0 | MPa | |
| Screw Speed | 40 - 75 | rpm |
| Injection instructions |
|---|
| Cylinder Temperature 4: 190 to 220°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fainplast PVC CKL 91/T-UV | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Dutral® TER 4437 | Versalis S.p.A. | EPDM | Dutral® |
| Lumid® SG2300B(W) | LG Chem Ltd. | Nylon 66 | Lumid® |
| Daelim Po1y® XP6070 | DAELIM INDUSTRIAL CO., LTD. | mHDPE | Daelim Po1y® |
| 3M™ Dyneon™ PTFE Compound NST 1111R | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |