80 MELT FLOW MEDIUM IMPACT COPOLYMER POLYPROPYLENE FOR INJECTION MOLDING

Pinnacle Polymers Polypropylene 2180H is made via UNIPOL™ PP technology, which utilizes gas-phase fluidized bed reactors with a high activity catalyst system to ensure uniform physical properties and lot-to-lot consistency.

This controlled rheology copolymer is intended for use in thin wall injection molded packaging, housewares and consumer products applications. High Melt Flow dramatically improves cycle-times without forfeiting impact. Contains nucleator and antistat.

The 2180H product provides:

High stiffness

Excellent impact at 23°C and -30°C

Very high melt flow

Excellent mold release

Superior processability

Excellent lot-to-lot consistency

Pinnacle's 2180H polypropylene is covered under US FDA Food Contact Notification 864. As such, this polymer can be used in contact with all food types under Conditions of Use A-H, as described in 21 CFR 176.170, Tables 1 and 2. This polymer also complies with 21 CFR 177.1520(c), items 3.1(a) and 3.2(a).

General Information
Additive	Antistatic Nucleating Agent
Features	Antistatic Controlled Rheology Food Contact Acceptable Good Mold Release Good Processability High Flow High Stiffness Impact Copolymer Low Temperature Impact Resistance Medium Impact Resistance Nucleated
Uses	Consumer Applications Household Goods Thin-walled Packaging
Agency Ratings	FDA 21 CFR 176.170 Table 1 & 2, Cond A-H FDA 21 CFR 177.1520(c) 3.1a FDA 21 CFR 177.1520(c) 3.2a
Forms	Pellets
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	0.900	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	74 to 86	g/10 min	ASTM D1238
Molding Shrinkage - Flow	1.4	%	ASTM D955

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Yield, 3.20 mm, Injection Molded)	> 20.0	MPa	ASTM D638
Tensile Elongation ²(Yield, 3.20 mm, Injection Molded)	5.0	%	ASTM D638
Flexural Modulus - 1% Secant ³(3.20 mm, Injection Molded)	> 1070	MPa	ASTM D790A

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact ⁴(23°C, 3.20 mm, Injection Molded)	> 96	J/m	ASTM D256
Notched Izod Impact (Area) ⁵(23°C, 3.20 mm, Injection Molded)	> 9.40	kJ/m²	ASTM D256
Gardner Impact ⁶(-30°C)	14.0	J	ASTM D5420

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	106	°C	ASTM D648

Note Message
1 .	Type I, 51 mm/min
2 .	Type I, 51 mm/min
3 .	Type I, 1.3 mm/min
4 .	Type I
5 .	Type I
6 .	Method G, Geometry GC

Resin Grade	Manufacturer	Category	Trademark
SHIN-A SEB-140A75	SHIN-A T&C	Epoxy	SHIN-A
Wellamid® XT1863-BK1	Wellman Engineering Resins	Nylon 66	Wellamid®
XANTAR® C MC 3440	Mitsubishi Engineering-Plastics Corp	PC+ABS	XANTAR® C
ARK 2150-60A	Arkadia Plastics, Inc.	TPU-Polyester	ARK
PLUSTEK RA303G7	Polyram Ram-On Industries	Nylon 66	PLUSTEK