Marlex® HMN 6060UV

Category:	HDPE , High Density Polyethylene
Manufacturer:	Saudi Polymers Company
Trademark:	Marlex®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Ce0MQk_Marlex-HMN-6060UV.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

This hexene copolymer is tailored for injection moulding applications that require:

Moderate flow

Good impact strength

Excellent stiffness

Durable and recyclable for sustainability

Strong UV resistance

Typical injection moulded applications for HMN 6060UV include items such as:

Crates (indoor and outdoor use)

Tote boxes

Structural foam (with proper foaming agent)

General Information
Features	Rigidity, high Copolymer hexene comonomer Impact resistance, good Good UV resistance Foamable property Recyclable materials Medium liquidity Durability Compliance of Food Exposure
Uses	Structural Foam Tools/Parts Box Loading box
Agency Ratings	ASTM D 4976-PE243 FDA 21 CFR 177.1520(c) 3.2a Europe No 10/2011
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	0.963	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	6.0	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance (100% Igepal, Compression Molded, F50)	< 20.0	hr	ASTM D1693B

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, Compression Molded)	66		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Yield, Compression Molded)	33.0	MPa	ASTM D638
Tensile Elongation ²(Break, Compression Molded)	990	%	ASTM D638
Flexural Modulus			ASTM D790
1% secant : Molding	1670	MPa	ASTM D790
Tangent : Molding	2500	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C, Compression Molded)	35	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648A
0.45 MPa, unannealed, molded	81.0	°C	ASTM D648A
1.8 MPa, unannealed, molded	51.0	°C	ASTM D648A
Brittleness Temperature ³	< -75.0	°C	ASTM D746A
Vicat Softening Temperature	127	°C	ASTM D1525 ⁴

Additional Information
The physical properties were determined on compression moulded specimens that were prepared in accordance with Procedure C of ASTM D4703, Annex A1.

Note Message
1 .	Type 4, 51mm/min
2 .	Type 4, 51mm/min
3 .	Type I specimen
4 .	速率 A (50°C/h), 压力1 (10N)

Resin Grade	Manufacturer	Category	Trademark
Spartech Polycom PP7000 B1	Spartech Polycom	PP Copolymer	Spartech
Hanwha Total PP HY300	HANWHA TOTAL PETROCHEMICALS Co., Ltd.	PP Homopolymer	Hanwha Total PP
INEOS HDPE J60-1700-173	INEOS Olefins & Polymers USA	HDPE	INEOS HDPE
LNP™ THERMOCOMP™ RB004 compound	SABIC Innovative Plastics	Nylon 66	LNP™ THERMOCOMP™
SQUARE® SR8656A/B	Shenzhen SQUARE Silicone Co., Ltd.	Silicone Rubber, LSR	SQUARE®