Electrafil® ABS-1200/SD
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Electrafil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CdnYcL_Electrafil-ABS-1200-SD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Base resin is alloyed with an inherently dissipative polymer to achieve permanent static dissipative capabilities without sacrificing appearance or colorability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 40.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 20 | % | ASTM D638 |
| Flexural Modulus | 1860 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 53.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 320 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 79.4 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+11 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 to 76.7 | °C | |
| Drying Time | 4.0 to 16 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 193 | °C | |
| Middle Temperature | 204 | °C | |
| Front Temperature | 199 | °C | |
| Nozzle Temperature | 199 | °C | |
| Processing (Melt) Temp | 196 | °C | |
| Mold Temperature | 32.2 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9925-65 Natural | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| AMTOPP CM25 | Inteplast Group | PP, Unspecified | AMTOPP |
| Cawiton® SN940 | Wittenburg B.V. | SEBS | Cawiton® |
| LEXAN™ EXL1810T resin | SABIC Innovative Plastics | PC | LEXAN™ |
| OTECH TPR OTR5505-Soles | OTECH Corporation | TPE | OTECH TPR |