Sasol Polymers PP HHR102

Category:	PP Homopolymer , Polypropylene Homopolymer
Manufacturer:	Sasol Polymers
Trademark:	Sasol Polymers PP
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	CdEpUS_Sasol-Polymers-PP-HHR102.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Features

Low flow

Low water carry over during the extrusion process

Good mechanical strength and properties

Suitable for moulding of thick walled general purpose articles

Applications
Extrusion

Fine slit film tape for woven and packaging fabric, e.g. heavy duty bags or flexible intermediate bulk containers (FIBC's)

Packaging strapping

Flat sheet for use in thermoforming applications

Monofilaments for use in ropes, twines, nets and bristles

Coarse slit film tape for ropes and twines

Injection moulding

Domestic, industrial and general purpose articles

Blow moulding

Mouldings up to 1 litre in capacity

General Information
Additive	Processing stabilizer
Features	Homopolymer Good processing stability Good strength Low liquidity Compliance of Food Exposure Low water portability General
Uses	Films monofilament Industrial application Thick wall fittings (parts) Household goods Belt material Sheet General Heavy packing bag
Agency Ratings	EC 1935/2004 FDA 21 CFR 177.1520(a)(3)(i)(c)(1) FDA 21 CFR 177.1520(c) 3.1a
Forms	Particle
Processing Method	Film extrusion Blow molding Extrusion Sheet extrusion molding Injection molding

Physical	Nominal Value	Unit	Test Method
Density	0.905	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	2.0	g/10 min	ISO 1133
Molding Shrinkage			ISO 294-4
Vertical flow direction	1.4	%	ISO 294-4
Flow direction	1.5	%	ISO 294-4

Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness	70.0	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	1650	MPa	ISO 527-2/1A/1
Tensile Stress (Yield)	35.0	MPa	ISO 527-2/1A/50
Tensile Strain			ISO 527-2/1A/50
Yield	9.0	%	ISO 527-2/1A/50
Fracture	> 50	%	ISO 527-2/1A/50
Flexural Modulus	1600	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	4.0	kJ/m²	ISO 179/1eA

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	85.0	°C	ISO 75-2/B
1.8 MPa, not annealed	53.0	°C	ISO 75-2/A
Vicat Softening Temperature
--	154	°C	ISO 306/A120
--	90.0	°C	ISO 306/B120
Melting Temperature	163	°C	ISO 11357-3

Injection	Nominal Value	Unit
Hopper Temperature	40.0 - 60.0	°C
Rear Temperature	180 - 260	°C
Middle Temperature	220 - 280	°C
Front Temperature	240 - 280	°C
Nozzle Temperature	220 - 280	°C
Processing (Melt) Temp	220 - 280	°C
Mold Temperature	20.0 - 60.0	°C

Injection instructions
Zone 4: 240 to 280°C

Extrusion	Nominal Value	Unit
Hopper Temperature	40.0 - 60.0	°C
Cylinder Zone 1 Temp.	220 - 280	°C
Cylinder Zone 2 Temp.	240 - 280	°C
Cylinder Zone 3 Temp.	240 - 280	°C
Cylinder Zone 4 Temp.	240 - 280	°C
Cylinder Zone 5 Temp.	240 - 280	°C
Melt Temperature	220 - 280	°C
Die Temperature	240 - 260	°C

Resin Grade	Manufacturer	Category	Trademark
TEREZ PA 6 7400 GK 30	TER HELL PLASTIC GMBH	Nylon 6	TEREZ PA 6
Boda BDT-LB3752	Chenguang Fluoro & Silicone Elastomers Co., Ltd.	Fluorelastomer	Boda
APICAL 120AF616	Kaneka Corporation	PI, TS	APICAL
Elastollan® 1164D	BASF Corp. Thermoplastic Polyurethanes	TPU-Polyether	Elastollan®
Karina CLEAR PVC COMPOUND 70/213-D-IS-SD	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina