INEOS PP N00M-00
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | INEOS Olefins & Polymers USA |
| Trademark: | INEOS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Cd0ngF_INEOS-PP-N00M-00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| N00M-00 is a fractional melt flow rate, medium term heat aging high impact copolymer polypropylene for blow molding, pipe, tubing and sheet extrusion applications. It offers a superior balance of stiffness and impact strength as compared to competitive impact copolymers of similar melt flow rate. This material meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520. This product is not recommended for taste or odor sensitive applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.902 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.45 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 77 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 25.2 | MPa | |
| Break | 23.1 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 9.6 | % | |
| Break | 480 | % | |
| Flexural Modulus - 1% Secant | 1190 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 120 | J/m | |
| 23°C | 970 | J/m | |
| Notched Izod Impact (Area) (23°C) | 95.2 | kJ/m² | ASTM D256 |
| Instrumented Impact, Ductility | ASTM D3763 | ||
| -20°C | Ductile | ||
| 23°C | Ductile |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 87.8 | °C | |
| 1.8 MPa, Unannealed | 57.8 | °C | |
| Brittleness Temperature | -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 151 | °C | ASTM D1525 |
| RTI Elec | 48.9 | °C | UL 746 |
| RTI Imp | 48.9 | °C | UL 746 |
| RTI Str | 48.9 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60°) | 56 | ASTM D2457 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Medalist® MD-575D | Teknor Apex Company | TPE | Medalist® |
| XYLEX™ X7519HP resin | SABIC Innovative Plastics | PC+Polyester | XYLEX™ |
| ALCOM® PA6 900/1 MO1 | ALBIS PLASTIC GmbH | Nylon 6 | ALCOM® PA6 |
| Karina LILAC PVC COMP -E KAPU 6534/190-NT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 9077-75 Yellow 4181 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |