Fluoraz FEPM 790
| Category: | FEP , Perfluoroethylene Propylene Copolymer |
| Manufacturer: | Greene, Tweed & Co. |
| Trademark: | Fluoraz |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CcMttf_Fluoraz-FEPM-790.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Fluoraz FEPM 790 is a Perfluoroethylene Propylene Copolymer (FEP) product. It is available in North America. |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.60 | g/cm³ | ASTM D297 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 95 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (50% Strain) | 10.7 | MPa | ASTM D412 |
| Tensile Strength (Break) | 24.1 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 130 | % | ASTM D412 |
| Compression Set 1 | ASTM D395 | ||
| 23°C, 70 hr | 16 | % | |
| 175°C, 166 hr | 27 | % | |
| 200°C, 22 hr | 21 | % |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (276°C, 70 hr) | -46 | % | ASTM D573 |
| Change in Ultimate Elongation in Air (276°C, 70 hr) | -11 | % | ASTM D573 |
| Change in Durometer Hardness in Air (276°C, 70 hr) | 0.0 | ASTM D573 | |
| Change in Tensile Strength | ASTM D471 | ||
| 135°C, 70 hr, in Ford ATF | -16 | % | |
| 135°C, 70 hr, in MIL-H-5606 | -27 | % | |
| 135°C, 70 hr, in Wagner 21B | -22 | % | |
| 175°C, 70 hr, in Stauffer 7700 Fluid | -27 | % | |
| Change in Ultimate Elongation | ASTM D471 | ||
| 135°C, 70 hr, in Ford ATF | 18 | % | |
| 135°C, 70 hr, in MIL-H-5606 | 21 | % | |
| 135°C, 70 hr, in Wagner 21B | 34 | % | |
| 175°C, 70 hr, in Stauffer 7700 Fluid | 28 | % | |
| Change in Durometer Hardness | ASTM D471 | ||
| 135°C, 70 hr, in Ford ATF | -3.0 | ||
| 135°C, 70 hr, in Stauffer 7700 Fluid | -11 | ||
| 135°C, 70 hr, in Wagner 21B | -8.0 | ||
| Change in Volume | ASTM D471 | ||
| 135°C, 70 hr, in Ford ATF | 8.0 | % | |
| 135°C, 70 hr, in MIL-H-5606 | 23 | % | |
| 135°C, 70 hr, in Wagner 21B | 8.3 | % | |
| 175°C, 70 hr, in Stauffer 7700 Fluid | 21 | % | |
| Change in Flexural Strength - in Wagner 21B 2(135°C) | -8 Points | ASTM D471 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature | -7 to 232 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rubber Classification | FEPM | ASTM D1418 | |
| TR 10/50 | 4 | °C | ASTM D1329 |
| Note Message | |
|---|---|
| 1 . | In air, 25% of original deflection |
| 2 . | 70 hrs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen RP344N | PolyMirae | PP Random Copolymer | Moplen |
| TRIMID® N66-G43HL | Polymer Technology and Services, LLC | Nylon 66 | TRIMID® |
| Boltaron 1050E | Boltaron Performance Products | PVC, Unspecified | Boltaron |
| Karina IVORY PVC COMPOUND 90901-35/ 1-D-AC-AS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ESTOPLAST XU 4201GY41 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |