LONGLITE® PMC T 385 J70
| Category: | Phenolic , Phenolic |
| Manufacturer: | CCP Group |
| Trademark: | LONGLITE® PMC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CcLGdh_LONGLITE-PMC-T-385-J70.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PMC T 385 J70 is a wood flour- and mineral-reinforced phenolic injection moulding compound with improved heat resistance |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | 0.80 - 1.3 | % | ISO 2577 |
| Water Absorption | |||
| 24 hr | 0.33 | % | ASTM D570 |
| 23°C, 24 hr | 0.33 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield | 41.0 | MPa | ISO 527-2 |
| -- | 41.0 | MPa | ASTM D638 |
| Flexural Strength | 95.0 | MPa | ASTM D790, ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 164 | °C | ASTM D648, ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.4E+10 | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | 1.0E+12 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength (2.00 mm) | 10 | kV/mm | ASTM D149, IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (6.34 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| Spiral Flow, CCP: 60 to 70 cmHeat Resistance, IEC 60216-P1, 2 hr: 180°CCharpy Impact, JIS K7111: 3.6 kg cm/cm² |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 40.0 - 90.0 | °C | |
| Middle Temperature | 40.0 - 90.0 | °C | |
| Front Temperature | 40.0 - 90.0 | °C | |
| Nozzle Temperature | 85.0 - 105 | °C | |
| Processing (Melt) Temp | 110 - 120 | °C | |
| Mold Temperature | 165 - 195 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | < 1.00 | MPa | |
| Screw Speed | 30 - 50 | rpm |
| Injection instructions |
|---|
| Injection Time: 5 ± 2 secHardening Time: 15 ± 5 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® ECO315 BK06 | Ascend Performance Materials Operations LLC | Nylon 66/6 | Vydyne® |
| DynaChar™ C166 | Polymer Dynamix | Polyolefin, Unspecified | DynaChar™ |
| DOW™ Electrical & Telecommunications HFDG-4201 NT | The Dow Chemical Company | LDPE | DOW™ Electrical & Telecommunications |
| LEXAN™ IR2840 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Sylvin 8627-70 Clear Black 275 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |