Pyramid™ PEKK Plus® KK4150-NT
| Category: | PAEK , Polyaryletherketone |
| Manufacturer: | Polymics, Ltd. |
| Trademark: | Pyramid™ PEKK Plus® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CbazWS_Pyramid-PEKK-Plus-KK4150-NT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyaryletherketone, High Flow, 30% Glass Filled |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.040 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 103 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12400 | MPa | ASTM D638 |
| Tensile Strength | 186 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 11000 | MPa | ASTM D790 |
| Flexural Strength | 255 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (0.318 mm) | 8.0 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 321 | °C | ASTM D648 |
| Glass Transition Temperature | 177 | °C | ASTM E1356 |
| Melting Temperature | 360 | °C | DSC |
| CLTE - Flow | 1.6E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.1 | ohms | ASTM D257 |
| Volume Resistivity | 2.5 | ohms·cm | ASTM D257 |
| Dielectric Strength | 240 | kV/mm | ASTM D149 |
| Dielectric Constant | 3.30 | ASTM D150 | |
| Dissipation Factor | 4.0E-3 | ASTM D150 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA III HDPE2208J | ROMPETROL PETROCHEMICALS S.R.L. | HDPE | MIDILENA III |
| Styrolution PS 5801 | INEOS Styrolution Group GmbH | PS (HIPS) | Styrolution PS |
| UMG ALLOY® TA-820CA | UMG ABS, Ltd. | ASA+PC | UMG ALLOY® |
| OpteSTAT™ PBT DP492x1 | Ovation Polymers Inc. | PBT | OpteSTAT™ |
| PERLER® N09V4000B01 | A.D. Compound S.p.A. | PP Homopolymer | PERLER® |