INLUBE PA6SI2
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Infinity LTL Engineered Compounds |
| Trademark: | INLUBE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CbBtGl_INLUBE-PA6SI2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Specific Volume | 0.893 | cm³/g | |
| Molding Shrinkage - Flow | 1.3 to 1.6 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.5 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 72.4 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 50 | % | ASTM D638 |
| Flexural Modulus | 2760 | MPa | ASTM D790 |
| Shear Strength | 65.5 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 59 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 1600 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 71.1 | °C | ASTM D648 |
| CLTE - Flow | 8.3E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 249 to 288 | °C | |
| Mold Temperature | 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.013 to 0.025 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| QR Resin QR-2008-FR | QTR, Inc. | ABS | QR Resin |
| Styropor® P-440H | BASF Corporation | PS (EPS) | Styropor® |
| MAJORIS EE115T - 8938 | AD majoris | PP, Unspecified | MAJORIS |
| LUVOCOM® 80-8842 | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |
| FUDOWPREMIX® FP100F typeB | Fudow Co., Ltd. | Polyester, TS | FUDOWPREMIX® |