Sumitomo Phenolic FM 4008
| Category: | Phenolic , Phenolic |
| Manufacturer: | Sumitomo Bakelite North America, Inc. |
| Trademark: | Sumitomo Phenolic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Can0nu_Sumitomo-Phenolic-FM-4008.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FM 4008 is a fiberglass and mineral reinforced phenolic resole compound, with excellent dimensional stability and good strength at elevated temperatures. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.80 | g/cm³ | ASTM D792 |
| Apparent Density | 0.80 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow (Compression Molded) | 0.20 | % | ASTM D955 |
| Water Absorption - 48 hr | 0.15 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale, Compression Molded) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Compression Molded) | 50.0 | MPa | ASTM D638 |
| Flexural Modulus (Compression Molded) | 14000 | MPa | ASTM D790 |
| Flexural Strength (Compression Molded) | 140 | MPa | ASTM D790 |
| Compressive Strength | 240 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 27 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, Compression Molded | 265 | °C | |
| 1.8 MPa, Annealed, Compression Molded | > 282 | °C | |
| CLTE - Flow | 1.9E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | ASTM D149 | ||
| -- 2 | 15 | kV/mm | |
| -- 3 | 13 | kV/mm | |
| Arc Resistance | 180 | sec | ASTM D495 |
| Note Message | |
|---|---|
| 1 . | Wet, 60 Hz |
| 2 . | Method A (Short-Time) |
| 3 . | Method B (Step-by-Step) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIMID® N66-T100HL | Polymer Technology and Services, LLC | Nylon 66 | TRIMID® |
| CP PRYME® Polystyrene PS100-8M NAT | Chase Plastics Services Inc. | PS (GPPS) | CP PRYME® Polystyrene |
| Elastron® G G500.A23.B.PA | Elastron USA, Inc. | SEBS | Elastron® G |
| Karina CLEAR PVC COMPOUND -E 80/242-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ AB002 compound | SABIC Innovative Plastics | ABS | LNP™ THERMOCOMP™ |