VESTAKEEP® 2000 FC30
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Evonik Industries AG |
| Trademark: | VESTAKEEP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CZGuW0_VESTAKEEP-2000-FC30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Carbon fiber-reinforced, graphite and PTFE-filled polyether ether ketone VESTAKEEP 2000 FC30 is a medium-viscosity, carbon fiber-reinforced, graphite and PTFEfilled polyether ether ketone for injection molding. Parts made of this resin can be used for bearing bushing or gearbox parts, due to the self-lubricating effect. The semi-crystalline polymer features superior mechanical, thermal, and chemical resistance. Parts made from VESTAKEEP 2000 FC30 are self-extinguishing. VESTAKEEP 2000 FC30 can be processed by common injection-molding machines for thermoplastics. We recommend a melt temperature between 370°C and 380°C during the injection molding process. If temperatures exceed 380°C, toxic gases can be released. Adequate ventilation and protective equipment must be provided. The mold temperature should be within a range of 160°C to 200°C, preferably 180°C. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (380°C/5.0 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 180°C, 2.00 mm | 0.40 | % | |
| Flow : 180°C, 2.00 mm | 0.10 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 145 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C, Complete Break | 5.0 | kJ/m² | |
| 23°C, Complete Break | 6.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C, Complete Break | 40 | kJ/m² | |
| 23°C, Complete Break | 40 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 337 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 320 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 340 | °C | ISO 306/A |
| -- | 335 | °C | ISO 306/B |
| Melting Temperature 2 | 340 | °C | ISO 11357-3 |
| CLTE - Flow (23 to 55°C) | 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+5 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+7 | ohms·cm | IEC 60093 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 6.10 | ||
| 1 MHz | 4.90 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (2.00 mm) | 900 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 370 to 380 | °C | |
| Mold Temperature | 160 to 200 | °C |
| Note Message | |
|---|---|
| 1 . | determined on 2 mm sheets with film gate at rim mold temperature 180°C |
| 2 . | 2nd heating |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsamid® AESN Noir P212 CTL | Arkema | Nylon 12 | Rilsamid® |
| Tenite™ Propionate 360E0096916 Natural, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| TPX® RT31 | Mitsui Chemicals, Inc. | PMP Copolymer | TPX® |
| Toppyl SP2102C | LyondellBasell Industries | Polyolefin, Unspecified | Toppyl |
| Zhongfa PC/ABS CW-G20 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PC+ABS | Zhongfa |