DECAL® 2061
| Category: | Phenolic , Phenolic |
| Manufacturer: | Synres-Almoco BV |
| Trademark: | DECAL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CX3GrF_DECAL-2061.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Wood flour reinforced phenolic moulding compound Good electrical properties, chemical resistance and mechanical properties This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 to 1.40 | g/cm³ | ISO 1183 |
| Apparent Density | 0.50 to 0.70 | g/cm³ | ISO 60 |
| Molding Shrinkage - Flow 1 | 0.90 to 1.1 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | < 1.2 | % | ISO 62 |
| Post Shrinkage 2 | 0.50 to 0.70 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 4000 to 6000 | MPa | ISO 527-2 |
| Tensile Stress (Injection Molded) | 50.0 to 70.0 | MPa | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 6000 to 8000 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 90.0 to 110 | MPa | ISO 178 |
| Compressive Stress | 200 to 250 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Injection Molded) | 2.0 to 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (Injection Molded) | 6.0 to 9.0 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | 160 to 180 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 100 to 120 | °C | ISO 75-2/C |
| CLTE - Flow (50 to 150°C) | 3.5E-5 to 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.20 to 0.40 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 to 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 to 1.0E+17 | ohms·cm | IEC 60093 |
| Electric Strength | 20 to 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 16.0 12.0 | ||
| 1 MHz | 6.00 4.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.60 to 0.80 | ||
| 1 MHz | 0.060 to 0.080 | ||
| Arc Resistance | PLC 6 | ASTM D495 | |
| Comparative Tracking Index | > 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm, Tested by Synres-Almoco) | V-0 | UL 94 | |
| Glow Wire Flammability Index | 900 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 900 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | 168 h / 110°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILPURAN® 6700/60 A/B | Wacker Chemie AG | Silicone | SILPURAN® |
| SILVER® PC2510.HF | Guangdong Silver Age Sci & Tech. Co., Ltd | PC+ABS | SILVER® |
| BJB Silicone TC-5040 A/B | BJB Enterprises, Inc. | Silicone | BJB Silicone |
| Karina GRAY PVC COMPOUND 800-18/101-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Loyblend® TK-1000 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PC+PET | Loyblend® |