Elastollan® C 90 A 15 HPM 000
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | BASF Polyurethanes GmbH |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CWsIiD_ElastollanC90A15HPM000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermoplastic Polyester-Polyurethane with excellent mechanical properties and chemical resistance, outstanding wear resistance, high tear and tensile strength, good damping characteristic and high resilience performance, high heat resistance and improved setting properties. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183/A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 3 sec) | 91 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 45.0 | mm³ | ISO 4649-A |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | DIN 53504-S2 | ||
| 20% strain | 4.00 | MPa | DIN 53504-S2 |
| 100% strain | 8.00 | MPa | DIN 53504-S2 |
| 300% strain | 13.0 | MPa | DIN 53504-S2 |
| Tensile Stress (Yield) | 45.0 | MPa | DIN 53504-S2 |
| Tensile Elongation (Break) | 600 | % | DIN 53504-S2 |
| Tear Strength 1 | 80 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 20 | % | ISO 815 |
| 70°C, 24 hr | 29 | % | ISO 815 |
| 100°C, 24 hr | 43 | % | ISO 815 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 152 | °C | ISO 306/A120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 40 | °C | |
| Rear Temperature | 195 - 210 | °C | |
| Middle Temperature | 200 - 220 | °C | |
| Front Temperature | 210 - 225 | °C | |
| Nozzle Temperature | 215 - 230 | °C | |
| Processing (Melt) Temp | 210 - 225 | °C | |
| Mold Temperature | 20 - 40 | °C | |
| Injection Rate | Slow | ||
| Back Pressure | 5.00 - 15.0 | MPa | |
| Screw L/D Ratio | 18.0:1.0 to 22.0:1.0 | ||
| Screw Compression Ratio | 2.0 : 1.0 - 3.0 : 1.0 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 160 - 180 | °C | |
| Cylinder Zone 2 Temp. | 170 - 190 | °C | |
| Cylinder Zone 3 Temp. | 180 - 200 | °C | |
| Cylinder Zone 4 Temp. | 195 - 215 | °C | |
| Adapter Temperature | 200 - 220 | °C | |
| Die Temperature | 195 - 215 | °C |
| Note Message | |
|---|---|
| 1 . | Method B, right-angle specimen (cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SITRALIN 15E-TF10-HK-GF10 / C6PS | SITRAPLAS GmbH | ASA+Nylon | SITRALIN |
| Dynalloy™ OBC 8100-N50 | PolyOne Corporation | TPE | Dynalloy™ |
| Eco-Solutions GP9001-N | MINIMA Technoloy Co. Ltd. | Biodeg Polymers | Eco-Solutions |
| KANEKA H536 | Kaneka North America LLC | CPVC | KANEKA |
| PENTAMID B GV15 H schwarz | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |