Alkathene® Ultra LDH210
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Qenos Pty Ltd |
| Trademark: | Alkathene® Ultra |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CVvW5L_Alkathene-Ultra-LDH210.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LDH210 is a low density polyethylene designed for the production of bundle shrink films as well as a variety of medium gauge (40 - 80µm) general purpose film applications. LDH210 is formulated with a process stabilisation additive package but contains no antiblock or slip additives. LDH210 is intended for use in bundle shrink films as well as a variety of medium gauge (40 - 80µm) applications including produce bags, carry bags and blending into other film grades. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 50 µm, blown film | 140 | MPa | ASTM D882 |
| 2% secant, TD : 50 µm, blown film | 170 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 50 µm, blown film | 11.0 | MPa | ASTM D882 |
| TD : Yield, 50 µm, blown film | 10.0 | MPa | ASTM D882 |
| MD : Broken, 50 µm, blown film | 23.0 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 18.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 360 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | 770 | % | ASTM D882 |
| Dart Drop Impact (50 µm, Blown Film) | 120 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, blown film | 520 | g | ASTM D1922 |
| TD : 50 µm, blown film | 330 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Blown Film) | 73 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 6.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties taken from blown film processed at a blow up ratio of 2:1. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Delta PP 108 | Delta Polymers | PP Homopolymer | Delta |
| HANWHA EVA 1834 | Hanwha Chemical | EVA | HANWHA EVA |
| Hostalen GD 7255 LS | LyondellBasell Industries | HDPE | Hostalen |
| OTECH TPO OTR5088-Molding | OTECH Corporation | TPE | OTECH TPO |
| ULTEM™ SF2350 resin | SABIC Innovative Plastics Asia Pacific | PEI | ULTEM™ |