| VA-1710 is a 70 shore A polyurethane elastomer formulated for hand-batch processing, vacuum assisted processing or meter mix dispensed. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury. MOCA, or TDI. VA-1710 has excellent green strength for quick demold times. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Cured | 1.12 | g/cm³ | |
| Hardener | 1.14 | g/cm³ | |
| Base Resin | 1.21 | g/cm³ | |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D2566 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 70 Mix Ratio by Volume: 63 | ||
| Demold Time | 60 to 120 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.48 | Pa·s | |
| 25°C 2 | 1.1 | Pa·s | |
| 25°C 3 | 4.5 | Pa·s | |
| Curing Time 4 | 25 | hr | |
| Gel Time | 8.0 to 12 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 65 to 75 | ASTM D2240 | |
| Tensile Strength | 4.27 | MPa | ASTM D638 |
| Tensile Elongation at Break | 90 | % | ASTM D638 |
| Tear Strength | 10.5 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Mixed |
| 3 . | Resin |
| 4 . | 24 hours at 77°F + 1 hour at 150°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1200 T-70A | RTP Company | TPU-Polyether | RTP |
| EVATHENE® UE634-04 | USI Corporation | EVA | EVATHENE® |
| LNP™ LUBRICOMP™ SP003 compound | SABIC Innovative Plastics | Nylon 12 | LNP™ LUBRICOMP™ |
| ADENE® B36VYBG-02 | A.D. Compound S.p.A. | PP Copolymer | ADENE® |
| EPAMOULD 295A83W40 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |