Spartech Polycom SC14F-1060L
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Spartech Polycom |
| Trademark: | Spartech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CUgdCh_Spartech-Polycom-SC14F-1060L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Spartech SC14F-1060L is an unreinforced, flame retardant, nylon 6/6 resin for injection molding applications. It is heat stabilized and lubricated for good processing characteristics and easy mold release. This product meets Underwriter's Laboratories 94 V-0 flammability classification down to a thickness of 0.030" and 94 5VA down to 0.125" in thickness. Nylons are highly crystalline resins with a sharp melting and freezing point. That characteristic allows for good flow properties when in the melt state, and fast cycle times when cooling in the mold. The highly crystalline characteristic also brings high strength properties and wear resistance. A very versatile product for a wide variety of applications, Spartech SC14F-1060L is recommended for industrial, transportation, sporting goods and electrical/electronic applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 58.6 | MPa | ASTM D638 |
| Flexural Strength (23°C) | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 220 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.787 mm, NC | V-0 | UL 94 | |
| 3.18 mm, NC | 5VA | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 87.8 - 93.3 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 238 - 260 | °C | |
| Middle Temperature | 249 - 271 | °C | |
| Front Temperature | 249 - 271 | °C | |
| Nozzle Temperature | 243 - 254 | °C | |
| Processing (Melt) Temp | 238 - 260 | °C | |
| Mold Temperature | 21.1 - 93.3 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIBIT® 1500GN30 | Samyang Corporation | PBT | TRIBIT® |
| DINALON® B1X25 G30 W | Grupo Repol | Nylon 6 | DINALON® |
| HAIPLEN EP50 T3 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| Karina GRAY PVC COMPOUND -E 820-18/100-CR | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Pacrel® 6385N | Nanjing Jinling OPTA Polymer Co., Ltd. | TPV | Pacrel® |