Borealis PP HK060AE
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CTtiKF_Borealis-PP-HK060AE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HK060AE is a special low viscosity polypropylene homopolymer compound developed to fit the production of Glass Matt reinforced Thermoplastics. This material is also suitable as base resin for the production of PP-GF composites in the direct LFT compression and injection moulding process as well as in combination with LGF concentrates on the injection moulding process. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 130 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.5 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 132/10) | 78.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1600 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 35.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 8.0 | % | |
| Break | 15 | % | |
| Flexural Modulus 1 | 1550 | MPa | ISO 178 |
| Flexural Stress | 45.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 0.80 | kJ/m² | |
| -20°C | 0.90 | kJ/m² | |
| 23°C | 1.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 11 | kJ/m² | |
| 23°C | 55 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 1.6 | kJ/m² | |
| 23°C | 1.8 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 91.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 54.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 153 | °C | ISO 306/A50 |
| -- | 96.0 | °C | ISO 306/B50 |
| CLTE - Flow (-30 to 80°C) | 9.0E-5 | cm/cm/°C | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 220 to 270 | °C | |
| Mold Temperature | 30.0 to 60.0 | °C | |
| Injection Rate | Slow-Moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SFN10010 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Stirofor® HI-V2 NATURALE | SO.F.TER. SPA | PS (HIPS) | Stirofor® |
| ALTECH® PA66 A 2035/507 GF35 EF | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| Colorite G Series 8312G-015 | Colorite Polymers | PVC, Flexible | Colorite G Series |
| ECOVYLOPET® EMC2301E | TOYOBO America, Inc. | PET | ECOVYLOPET® |