Synthos EPS® 0513S/CZ
| Category: | PS (EPS) , Expanded Polystyrene |
| Manufacturer: | Synthos S.A. |
| Trademark: | Synthos EPS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CThMIU_Synthos-EPS-0513S-CZ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Synthos EPS®/CZ types 0308S, 0513S, 0814S and 1020S are expandable polystyrene (EPS) formed by spherical polystyrene particles that contains a hydrocarbon blowing agent. The material is surface treated against gluing during processing and the formation of electrostatic charge. Synthos EPS® 0513S/CZ (Koplen 0513S) is mainly used for production of shaped parts with wall thickness above 10 mm (e.g. shipping packaging for glass and electrical goods); production of smaller blocks with higher density or cutted profiles. |
| General Information | |
|---|---|
| Additive |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Density 1 | 0.02 to 0.04 | g/cm³ | Internal Method |
| Moisture Content | < 10000 | ppm | Internal Method |
| Particle Size - >95% between | 500 to 1000 | µm | Internal Method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blowing Agent | < 7.0 | wt% | Internal Method |
| Note Message | |
|---|---|
| 1 . | The typical bulk density indicates values obtained during single-step pre-foaming on continuous pre-foaming devicesLower values of bulk density can be achieved only after multiple pre-expansion. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NuSil EPM-2410 | NuSil Technology | Silicone | NuSil |
| EverGlide® SG5920 | Polymer Dynamix | Nylon 46 | EverGlide® |
| Fainplast PVC PH 70/N1 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Sylvin 86042-75 Clear 8422 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LGE 121 | LG Polymers India Pvt. Ltd. | PS (EPS) | LGE |