LEMALLOY® BX528A-3
| Category: | PPE+Nylon 6 , Polyphenylene Ether + Nylon 6 |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | LEMALLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CSv4NU_LEMALLOY-BX528A-3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LEMALLOY® BX528A-3 is a Polyphenylene Ether + Nylon 6 (PPE+Nylon 6) material. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of LEMALLOY® BX528A-3: Rigid. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.15 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 28.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ||||
| Across Flow : 3.20 mm | 1.0 to 1.2 | -- | % | |
| Flow : 3.20 mm | 1.2 to 1.4 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 2500 | 1400 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 62.0 | 37.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 5.0 | 15 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 57 | 140 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2300 | 1400 | MPa | ISO 178 |
| Flexural Stress (23°C) | 91.0 | 60.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 18 | 66 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 165 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 85.0 | -- | °C | ISO 75-2/A |
| CLTE - Flow | 9.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 240 to 270 | °C | |
| Middle Temperature | 250 to 290 | °C | |
| Front Temperature | 250 to 290 | °C | |
| Nozzle Temperature | 250 to 290 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP04PET | Southern Polymer, Inc. | PET | PRIMALENE |
| Sindustris PP GP2301 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Novamid® 2620J | DSM Engineering Plastics | Nylon 6/6T | Novamid® |
| Nypol® PA C3 T30 NTLA010 NS304 | Petropol Industry and Trade of Polymers LTDA | Nylon 66/6 | Nypol® PA |
| RTP 1899 X 141360 Z | RTP Company | Acrylic (PMMA) | RTP |