Devcon Wear Guard™ High Load
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Devcon |
| Trademark: | Devcon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CRD7ra_Devcon-Wear-Guard-High-Load.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Alumina ceramic bead-filled epoxy system with outstanding abrasion resistance for severe service conditions with particulate greater than 1/8" Intended Use:
Product Features:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.20 | g/cm³ | |
| Specific Volume | 0.466 | cm³/g | |
| Solid content- by Volume | 100 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Temperature Resistance | |||
| Dry | 149 | °C | |
| Wet | 60 | °C | |
| Tensile Shear Adhesion | 10.2 | MPa | ASTM D1002 |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.060 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 87 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 29.0 | MPa | |
| Flexural Strength | 49.2 | MPa | ASTM D790 |
| Compressive Strength | 75.8 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow | 5.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant | 41.0 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 2.0 Mixing ratio by capacity: 2.0 | ||
| Component B | Mixing ratio by weight: 1.0 Mixing ratio by capacity: 1.0 | ||
| Pot Life (24°C) | 30 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cured 7 days @ 75°F |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Curing Time | 16 | hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® BGV HZ 15 Black | Radici Plastics | Nylon 6 | Radilon® |
| Shuang-Bang WM-0155H | Shuang-Bang Industrial Corp. | Film, TPU | Shuang-Bang |
| XANTAR® G4F 23 UR | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Bergamid™ B70 G30 H Natural UV | PolyOne Corporation | Nylon 6 | Bergamid™ |
| LNP™ LUBRICOMP™ RAL23 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |