E-RIALGLASS H 07 H 30 G
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | RIALTI Srl |
| Trademark: | E-RIALGLASS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CQmFgG_E-RIALGLASS-H-07-H-30-G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene homopolymer obtained by partial recycling of selected industrial scraps; 30% glass fiber chemically coupled; heat stabilized for prolonged exposure to high temperatures. Good mechanical properties High flowabilitylevel, specific for injection molding; available in versions black colore. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.1 | % | |
| Flow | 0.30 | % | |
| Ash Content | 30 | % | ISO 3451 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Oven Aging (150°C) | 1.4 | month | ISO 4577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 75 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, 23°C) | 80.0 | MPa | ISO 527-2/20 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2/20 |
| Flexural Modulus 1(23°C) | 5700 | MPa | ISO 178 |
| Flexural Stress (23°C) | 105 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 34 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 6.0 | kJ/m² | |
| 23°C | 8.5 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 139 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 124 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 335 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 200 to 240 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silopren® Electro 170 | Momentive Performance Materials Inc. | Silicone | Silopren® |
| Cardia Compostable™ B-MT02 (Flex) | Cardia Bioplastics™ | TPS+Copolyester | Cardia Compostable™ |
| Moplen HP2619 | LyondellBasell Industries | PP Homopolymer | Moplen |
| Sylvin 8260-80 White 1439 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| RONFALIN® ABS 1336 CA | A. Schulman Europe | ABS | RONFALIN® |