Generic PP Copolymer - Mineral
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CPvCmF_Generic-PP-Copolymer---Mineral.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PP Copolymer - Mineral This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.960 - 2.10 | g/cm³ | ASTM D792 |
| 23°C | 0.975 - 1.17 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 4.7 - 35 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 0.70 - 28 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 4.65 - 18.3 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.10 - 1.2 | % | ASTM D955 |
| 23°C | 0.81 - 1.2 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.020 - 0.050 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 40 - 90 | ASTM D785 | |
| 23°C | 70 - 76 | ISO 2039-2 | |
| Durometer Hardness (23°C) | 59 - 71 | ISO 868 | |
| Ball Indentation Hardness | 50.0 - 71.4 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 1000 - 3080 | MPa | ASTM D638 |
| 23°C | 1230 - 2620 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 10.0 - 30.7 | MPa | ASTM D638 |
| Yield, 23°C | 17.0 - 27.5 | MPa | ISO 527-2 |
| Fracture, 23°C | 17.0 - 45.0 | MPa | ASTM D638 |
| Fracture, 23°C | 14.5 - 25.0 | MPa | ISO 527-2 |
| 23°C | 16.9 - 24.3 | MPa | ASTM D638 |
| 23°C | 19.9 - 30.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 3.0 - 5.0 | % | ASTM D638 |
| Yield, 23°C | 2.8 - 8.1 | % | ISO 527-2 |
| Fracture, 23°C | 2.3 - 200 | % | ASTM D638 |
| Fracture, 23°C | 2.5 - 100 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 800 - 3510 | MPa | ASTM D790 |
| 23°C | 1260 - 2520 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 20.0 - 52.4 | MPa | ASTM D790 |
| 23°C | 19.9 - 50.5 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.3 - 25 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 39 - 96 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 30 - 250 | J/m | ASTM D256 |
| 23°C | 3.8 - 46 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength (23°C) | 18 - 80 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 104 - 153 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 72.0 - 126 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 55.0 - 70.8 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 48.5 - 65.5 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 50.0 - 142 | °C | ASTM D1525 |
| -- | 47.9 - 152 | °C | ISO 306 |
| Melting Temperature (DSC) | 165 | °C | ISO 3146 |
| CLTE - Flow | |||
| -- | 5.0E-5 - 7.3E-5 | cm/cm/°C | ASTM D696 |
| -- | 4.6E-5 - 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 7.5E+13 - 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+13 - 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 595 - 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | 847 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 550 - 753 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.8 - 88.0 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 205 - 210 | °C | |
| Middle Temperature | 209 - 226 | °C | |
| Front Temperature | 209 - 236 | °C | |
| Processing (Melt) Temp | 210 - 245 | °C | |
| Mold Temperature | 39.8 - 60.6 | °C | |
| Injection Pressure | 87.3 - 100 | MPa | |
| Holding Pressure | 52.5 - 52.9 | MPa | |
| Back Pressure | 0.300 - 0.525 | MPa | |
| Screw Speed | 50 - 75 | rpm | |
| Clamp Tonnage | 4.5 - 4.6 | kN/cm² |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP Copolymer - MineralThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx FPP5A30CC | The Matrixx Group, Inc. | PP, Unspecified | Matrixx |
| Staramide AG7 | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| Network Polymers Nylon 6 | Network Polymers, Inc. | Nylon 6 | Network Polymers Nylon |
| Nipol® DN214 | Zeon Chemicals L.P. | NBR | Nipol® |
| Karina CRYSTAL CLEAR PVC COMPOUND -E 80/224-IS-SD-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |