Celazole® (U-Series) U-60
| Category: | PBI , Polybenzimidazole |
| Manufacturer: | PBI Performance Products, Inc. |
| Trademark: | Celazole® (U-Series) |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CPtlWf_Celazole-U-Series-U-60.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Celazole U-60 PBI is an unfilled PBI polymer suitable for compression molding. U-60 is commonly molded and machined into precision parts for industrial, chemical and petrochemical industries; aerospace; glass making; liquid crystal display (LCD) panel manufacture; and photovoltaic (PV) panel manufacture. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | |
| Water Absorption (23°C, 24 hr) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| E-Scale | 104 | ||
| M-Scale | > 125 | ||
| Durometer Hardness (Shore D) | 95 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5860 | MPa | ASTM D638 |
| Tensile Strength | 159 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 6550 | MPa | ASTM D790 |
| Flexural Strength | 221 | MPa | ASTM D790 |
| Compressive Modulus | 5860 | MPa | ASTM D695 |
| Compressive Strength | ASTM D695 | ||
| -- 1 | 393 | MPa | |
| 10% Strain | 345 | MPa | |
| Coefficient of Friction | |||
| vs. Metal - Dynamic 2 | 0.18 | ||
| vs. Metal - Dynamic 3 | 0.16 | ||
| vs. Metal - Static 4 | 0.14 | ||
| vs. Metal - Static 5 | 0.16 | ||
| vs. Steel - Dynamic | 0.16 | ||
| vs. Steel - Static | 0.15 | ||
| Tensile Fatigue - % of stress to failure 6 | 35 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 28 | J/m | ASTM D256 |
| Unnotched Izod Impact | 590 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 435 | °C | ASTM D648 |
| Glass Transition Temperature | 427 | °C | DMA |
| CLTE - Flow | TMA | ||
| 24 to 149°C | 2.3E-5 | cm/cm/°C | |
| 199 to 299°C | 3.2E-5 | cm/cm/°C | |
| Thermal Conductivity (25°C) | 0.40 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 23 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 3.40 | ||
| 10 kHz | 3.40 | ||
| 100 kHz | 3.30 | ||
| Dissipation Factor | ASTM D150 | ||
| 1 kHz | 0.0 | ||
| 10 kHz | 3.0E-3 | ||
| 100 kHz | 0.034 | ||
| Arc Resistance | 185 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 58 | % | ASTM D2863 |
| Note Message | |
|---|---|
| 1 . | Yield |
| 2 . | Brass |
| 3 . | Aluminum |
| 4 . | Aluminum |
| 5 . | Brass |
| 6 . | 8.1 kpsi, 1000000 cycles, 1Hz |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Next Nylon 66 Prime Series PG33-01NC | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| ISPLEN® PM 750 AS | REPSOL | PP Homopolymer | ISPLEN® |
| Karina ORANGE PVC COMPOUND 300-32/119 (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ RF006XXZ compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| TECHNYL® B 230 GREY 1421 H | Solvay Engineering Plastics | Nylon 66/6 | TECHNYL® |